Abstract: Fe–Co alloys exhibit an excellent saturation magnetization, which makes them become a potential candidate for the high property magnetic particles in magnetorheological fluids (MRFs). How to decrease their coercivity and residual magnetization without sacrificing the saturation magnetization is a crucial problem to be solved. In this study, Fe–Co nanoparticles were prepared by DC arc discharge and further disposed through low temperature annealing in Ar atmosphere. The successful synthesis of Fe–Co nanoparticles was proved by x-ray diffraction and EDS. The vibrating sample magnetometer results revealed that the prepared Fe–Co nanoparticles had a saturation magnetization of 208 emu g−1, while the coercivity and remanent magnetization were 58 Oe and 5.8 emu g−1, respectively. The MR properties of Fe–Co nanoparticles based MRFs (FeCoNP-MRFs) with 10% particles by volume fraction were systematically investigated. The FeCoNP-MRFs showed up to 4.61 kPa dynamic shear stress at 436 kA m−1 magnetic field and an excellent reversibility. The MR properties of FeCoNP-MRFs were fitted well by Bingham and power law model, and described by Seo-Seo and Casson fluid model. Meanwhile, the sedimentation ratio of FeCoNP-MRFs was still 87.3% after 72 h, indicating an excellent sedimentation stability.
https://doi.org/10.1088/1361-6528/acab07