Abstract :The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol (PVA) as binder by spray granulation method. The electromagnetic parameters of Fe and C composite particles were analyzed by vector network. The complex permittivity and magnetic permeability of Fe and C composite particles matched well with increasing C nanoparticle content, and then the microwave loss property was improved. A minimum reflection loss (RL) of -42.7 dB at 3.68 GHz for a composite with 4.6 mm in thickness can be obtained when the content ratio of the C nanoparticles, the modified Fe nanoparticles and the PVA is 21:49:30 (Sample 3)